Accreditation from renowned organizations from Europe and UK, for Accelerated Weatherability Test (Artificial weathering up to 10000 hours), Mechanical properties & Chemical composition of our formulation.
| Sl. No. | Properties | Standards | Range | Result | Accreditations From |
|---|---|---|---|---|---|
| 01 | Flexural Modulus of Elasticity | BS EN ISO 178:2013 | Not less than 2200 N/mm2 | 3070 N/mm2 | SK Z-Germany & BSI-UK |
| 02 | Tensile Impact Strength | BS EN ISO 8256:2005 | Not less than 600 KJ/m2 | 934 KJ/m2 | SK Z-Germany & BSI-UK |
| 03 | Accelerated Weathering [10000 Hours @ 20 GJ/m2] | DIN EN 513 | ΔE not more than 5 | 1.9 | SK Z-Germany & BSI-UK |
| 04 | Charpy Impact Strength | BS EN ISO 179 -2:1999 | Not less than 20 KJ/m2 | 74.4 KJ/m2 | SK Z-Germany & BSI-UK |
| 05 | Reduction in Charpy Impact Strength [Before & After Weathering] |
DIN EN ISO 179 -1/1fA | Not More than 40% | 10.4 % | SK Z-Germany |
| 06 | Vicat Softening Temperature | BS EN ISO 306:1997 | Not less than 75oC | 80oC | SK Z-Germany & BSI-UK |
| 07 | Heat Reversion @ 100o C, 60 Minutes | BS EN 12608-1:2016 | To comply as per EN 12608-1:2016 | Pass | BSI-UK |
| 08 | Resistance to Impact of Main Profile by falling Mass @-10oC, | BS EN 12608-1:2016 | To comply as per EN 12608-1:2016 | Pass | BSI-UK |
| 09 | Weld Strength (Individual Specimen) | BS EN 514:2000 | Not less than 20 Mpa | 25.32 Mpa | BSI-UK |
| 10 | Heat Aging @ 150oC,30 Minutes, | BS EN 12608-1;2016 | To comply as per EN 12608-1:2016 | Pass | BSI-UK |
| 11 | RoHS | DIRECTIVE 2011/65/EU | Lead should not be detected | Not detected | SGS |
| 12 | Flammability | UL-94 | 10 Sec | Vo | CIPET |
| 13 | Limiting Oxygen Index (LOI) | ASTM D2863 | 45% | 47% | CIPET |
| 14 | Density | ASTM D 792 | Not More than 1.5 gm/cc | 1.46 gm/cc | CIPET |
| 15 | Thermal Conductivity | ASTM E-1530 | 0.12 to 0.25 W/mk | 0.137 W/mk | CIPET |
| 16 | Co-efficient of Linear Thermal Expansion | ASTM D 696 | Below 5x10-5 / oC | 3.82x10-5 / oC | CIPET |